碲锰镉(CdMnTe)作为性能优异的室温核辐射探测器材料,可用于环境监测和工业无损检测领域。本文中采用Te溶剂Bridgman法生长In掺杂Cd_0.9Mn_0.1Te晶体,制备成10 mm×10 mm×2 mm大小的室温单平面探测器,研究了该探测器对²⁴¹Am@59.5 keV γ射线源的能谱响应。通过表征红外透过率、电阻率以及探测器能谱响应等参数,综合评定了探测器用CdMnTe晶体的质量、电学和探测器性能。结果表明,晶片的红外透过率均在55%以上,最好可达到60%。采用湿法钝化,100 V偏压下的漏电流由钝化前的9.48 nA降为钝化后的7.90 nA,钝化后的电阻率为2.832×10¹⁰ Ω·cm。在-400 V反向偏压下,CdMnTe探测器对²⁴¹Am@59.5 keV γ射线源的能量分辨率在钝化前后分别为13.53%和12.51%,钝化后的电子迁移率寿命积为1.049×10^-3 cm²/V。研究了探测器的能量分辨率随电压的变化特性,当偏压≤400 V时,探测器的能量分辨率主要由载流子的收集效率决定,而当偏压>400 V时,能量分辨率由漏电流决定。本文研究结果表明,Te溶剂Bridgman法生长的CdMnTe晶体质量较好,电阻率和电子迁移率寿命积满足探测器制备需求。     

三能级钾原子气体三维傅里叶变换频谱的解析解

利用投影切片定理、傅里叶位移定理和误差函数给出三能级钾原子气体三维傅里叶变换频谱在T=0界面的解析解.固定均匀线宽,非均匀展宽和对角线相关系数可以定量地识别,通过在适当方向上拟合三维傅里叶变换频谱谱峰的切片来确定.结果表明,非均匀展宽增大,频谱图沿着对角线方向延伸,对角线相关系数增大,频谱图逐渐变圆,振幅也逐渐变小.     

Eu:Lu2O3透明闪烁陶瓷的制备与性能

采用湿化学法合成了Eu原子掺量5%的Lu₂O₃陶瓷前驱体,通过SEM、XRD研究了煅烧前后前驱体和1 100 ℃煅烧4 h后粉体的形貌、结构以及物相。结果表明煅烧后的粉体为纳米类球形、高分散且结晶性良好的颗粒。颗粒尺寸为68.5 nm。使用煅烧后的粉体为原料,在1 650 ℃真空烧结30 h制备了高透过率的Eu:Lu₂O₃陶瓷,晶粒尺寸为46 μm,在611 nm处的直线透过率可以达到66.3%。此外对陶瓷的吸收曲线、光致激发和发射光谱特性以及X射线激发发射光谱进行研究。可观察到,Eu:Lu₂O₃陶瓷存在基质和激活离子两类吸收,光致发光光谱和X射线激发发射光谱均可以看出Eu:Lu₂O₃陶瓷存在极强的⁵D₀→⁷F₂跃迁发光,位于611 nm处。对比商业的BGO单晶的X射线发射光谱,可得本实验中制备的陶瓷的光输出为85 000 ph/MeV。Eu:Lu₂O₃陶瓷本身有着高X射线以及高能粒子的阻止能力,结合高光输出特性,表明Eu:Lu₂O₃陶瓷在X射线成像等领域具有巨大的潜在应用价值。     

Enhancing signal-to-noise ratio and resolution in low-field NMR relaxation measurements using post-acquisition digital filters

The traditional way to enhance signal-to-noise ratio (SNR) of nuclear magnetic resonance (NMR) signals is to increase the number of scans. However, this procedure increases the measuring time that can be prohibitive for some applications. Therefore, we have tested the use of several post-acquisition digital filters to enhance SNR up to one order of magnitude in time domain NMR (TD-NMR) relaxation measurements. The procedures were studied using continuous wave free precession (CWFP-T₁) signals, acquired with very low flip angles that contain six times more noise than the Carr–Purcell–Meiboom–Gill (CPMG) signal of the same sample and experimental time. Linear (LI) and logarithmic (LO) data compression, low-pass infinity impulse response (LP), Savitzky–Golay (SG), and wavelet transform (WA) post-acquisition filters enhanced the SNR of the CWFP-T₁ signals by at least six times. The best filters were LO, SG, and WA that have high enhancement in SNR without significant distortions in the ILT relaxation distribution data. Therefore, it was demonstrated that these post-acquisition digital filters could be a useful way to denoise CWFP-T₁, as well as CPMG noisy signals, and consequently reducing the experimental time. It was also demonstrated that filtered CWFP-T₁ method has the potential to be a rapid and nondestructive method to measure fat content in beef and certainly in other meat samples.     

Preparation and Characterization of Activated Carbon from Microwave and Conventional Heated Almond Shells Using Phosphoric Acid Activation

Activated carbon production from almond shells using phosphoric acid activation agent was achieved by applying both conventional heating and microwave heating in succession. The morphology and surface properties of activated carbon were studied using thermogravimetric and differential gravimetric analysis, Fourier-transform infrared spectroscopy, scanning electron microscopy, and Brunauer–Emmett–Teller analysis. A surface area of 1128 m²/g was achieved by optimizing the microwave power (500?W), microwave application time (15?minutes), conventional heating time (45?minutes), conventional heating temperature (500?°C), and the phosphoric acid:sample ratio (0.7:1). An adsorption capacity of methylene blue of 148?mg/g and an iodine value of 791?mg/g was obtained for the prepared activated carbon.     

焦炉上升管内壁结焦炭层的光谱学分析及结焦机理研究

以焦炉上升管内壁结焦炭层块为研究对象，采用X射线荧光光谱仪（XRF）、X射线衍射仪（XRD）、傅里叶红外光谱仪（FTIR）和激光共聚焦拉曼光谱仪（Raman）对结焦炭层的元素组成，以及各结焦炭层的矿物组成、组成结构和分子结构进行测试。分析从结焦炭层块外表面向内表面过渡的各结焦炭层的差异性，揭示焦炉上升管内壁结焦机理。结果表明焦炉上升管内粉尘中Fe，S和Cr极易催化荒煤气中蒽、萘等稠环芳烃化合物成炭，在焦炉上升管内壁形成炭颗粒沉积，为焦油凝结挂壁提供载体，在荒煤气温度降至结焦温度时易结焦积碳。结焦炭层均含有芳香层结构，随着结焦炭层从外表面向内表面过渡，各结焦炭层的面层间距(d₀₀₂)逐渐降低、层片直径(L_a)先降低后增加、层片堆砌高度(Lc)和芳香层数(N)先稳定后增加。结焦炭层石墨化过程是由结焦炭层内表面向外表面进行，主要包括其片层外缘的羧基和部分C-O结构的降解剥离，从而形成高度规整的共轭结构。结焦炭层块中C元素是以结晶碳与无定型碳的混合物形式存在。以上研究为解决焦炉上升管内壁结焦及腐蚀问题，提高换热器换热效率，有效回收焦炉荒煤气显热，降低焦化企业能耗提供实验基础和理论依据。     